Aziridine Crosslinking Agent CX-100 Alterntive Crosslinker

Crosslinking agent YY-100, alternative of CX-100 ,With YY-100, the original linear structure of the water-based resin can be modified through cross-linking to form a three-dimensional network structure. This significantly improves the coating's water resistance, adhesion strength, wet and dry abrasion resistance, and chemical resistance, while reducing deformation and significantly enhancing various coating properties.

Send Inquiry

Description

Crosslinking agent YY-100

Alternative of CX-100

Product Description

With YY-100, the original linear structure of the water-based resin can be modified through cross-linking to form a three-dimensional network structure. This significantly improves the coating's water resistance, adhesion strength, wet and dry abrasion resistance, and chemical resistance, while reducing deformation and significantly enhancing various coating properties.

YY-100 can be crosslinking in room temperature but better crosslinking speed when hearting at temperature 60-80°C. Normally 1-3% to the solid content ratio of the emulsion. The best to add when pH of emulsions is 8-9, avoid adding when emulsion Ph is below 7. After adding YY-100, should use within 24 hours to avoid gelling happen. YY-100 can be dissolved in water, alcohol, ketone and ester.

Product Parameters

Appearance	Light yellow transparent liquid
Non volatile Content,%	≥99.0%
Viscosity,(LVT2#, 6rpm @ 25℃),cps	100-400cps
S.G	1.03
Aziridine content	6.16 mol/kg